Ga-igbohunsafẹfẹ quenchingti wa ni okeene lo fun dada quenching ti ise irin awọn ẹya ara.O jẹ iru ọna itọju igbona irin ti o jẹ ki dada workpiece gbejade lọwọlọwọ ti o fa lọwọlọwọ, yara yara dada ti awọn apakan, ati lẹhinna yarayara quenching.Induction alapapo ohun elo, iyẹn ni, alapapo fifa irọbi iṣẹ, lati le dada quenching. ohun elo.
Ilana ti alapapo fifa irọbi: A fi iṣẹ ṣiṣẹ sinu afẹfẹ pẹlu paipu bàbà ṣofo ni sensọ, lẹhin iraye si igbohunsafẹfẹ agbedemeji tabi lọwọlọwọ alternating igbohunsafẹfẹ giga (ac), ti a ṣẹda ni dada pẹlu igbohunsafẹfẹ ti lọwọlọwọ ti o fa, dada workpiece tabi alapapo iyara agbegbe (awọn iṣẹju diẹ si awọn iwọn otutu ti 800 ~ 1000 ℃, mojuto tun wa nitosi iwọn otutu yara) lẹsẹkẹsẹ lẹhin awọn iṣẹju-aaya pupọ ni iyara fun sokiri (dip) itutu omi (tabi itutu agbaiye epo immersion) pipe iṣẹ ina immersion, Ṣe awọn workpiece dada tabi agbegbe lati se aseyori awọn ti o baamu líle awọn ibeere.
Ti a ṣe afiwe pẹlu mimu alapapo lasan, o ni:
1. Awọn alapapo iyara jẹ gidigidi sare, eyi ti o le faagun awọn ibiti o ti A body orilede otutu ati kikuru awọn orilede akoko.
2. Gan itanran cryptocrystalline martensite le ti wa ni gba lori dada ti awọn workpiece lẹhin quenching, ati awọn líle ni die-die ti o ga (2 ~ 3HRC) .Low brittleness ati ki o ga rirẹ agbara.
3. Awọn workpiece mu nipasẹ awọn ilana ni ko rorun lati oxidize ati decarbonize, ati paapa diẹ ninu awọn workpiece le ti wa ni taara jọ ati ki o lo lẹhin processing.
4, Layer lile ti jinlẹ, rọrun lati ṣakoso iṣẹ naa, rọrun lati mọ mechanization, adaṣe.
5, ina dada alapapo quenching
Pipa igbohunsafẹfẹ giga ti lo si iṣẹ-ṣiṣe ti o nilo lati jẹri iṣẹ ti fifuye alternating gẹgẹbi torsion ati atunse.O nilo Layer dada lati ru wahala ti o ga tabi wọ resistance ju mojuto, ati dada ti workpiece nilo lati ni okun.O dara fun irin pẹlu akoonu erogba A = 0.40 ~ 0.50%.